关键词：疲劳; 化学铣切; 铝合金; 断裂; WOHLER曲线

摘要：

铝合金的化学铣切已经成为航空与航天工业零件成形的可靠加工方法,尤其是在加工飞机蒙皮时要比用传统的机械加工方法优越得多。但化学铣切在一定程度上会降低材料的疲劳寿命,是由于存在于金属板材表面抗疲劳的残余压应力在化铣过程中释放后造成的。因此有必要考虑化铣工艺对飞机疲劳寿命的影响。通过对化学铣切的2024-T3包铝疲劳性能的研究,以及对大型薄形试片疲劳试验方法的探讨,确定该化学铣切工艺完全能满足民用飞机疲劳寿命的要求。

Fatigue feature of chemical milling on aluminium alloy

YUE Jun, LI Na

Chengdu Aircraft Industrial (Group)Corporation, Chengdu 610092, China

Abstract: Chemical milling on aluminium alloys has become a credible machining method for machining parts in the aviation and spaceflight industry.It is better than the tradition mechanism machining method in milling plane skin especially.However, the chemical milling can drop the fatigue life of materials, since residual compress stress on metal surface is released in this milling.Thus, the effect of the chemical milling on the plane fatigue life must be understood.The fatigue capability of chemical milling clad 2024-T3 has been studied, and some fatigue experiment methods on big and thin samples have been also investigated.The results ascertained that this chemical milling can satisfy the requirement of the civil aviation fatigue life.

Keywords: Fatigue; Chemical milling; Aluminium alloy; Fracture; WOHLER curve

2009, 35(4): 115-117  收稿日期: 2008-10-28;收到修改稿日期: 2009-1-7

基金项目: 

作者简介: 岳俊(1978-),男,四川成都市人,工程师,硕士研究生,主要从事理化检测工作。

参考文献

[1] 哈宽富.金属力学性质的微观理论[M].北京:科学出版社,1983.
[2] 蔡 泽.金属磨损与断裂[M].上海:上海交通大学出版社,1985.
[3] 陈德和.钢的缺陷[M].北京:机械工业出版社,1966.
[4] 黄克智.弹塑性断裂力学[M].北京:清华大学出版社,1985.
[5] 北京钢铁研究院金属物理室.工程断裂力学[M].北京:国防工业出版社,1977.
[6] 姚启均.金属力学性能试验常用数据手册[M].北京:机械工业出版社,1994.
[7] 刘振学.实验设计与数据处理[M].北京:化学工业出版社,2004.
[8] 王敬端.机械工程材料[M].重庆:重庆大学出版社,1994.
[9] 袁懋昶.断裂力学理论及其工程应用[M].重庆:重庆大学出版社,1989.
[10] 邓至谦.金属材料及热处理[M].长沙:中南工业大学出版社,1989.
[11] Tomposn N, Wadsworth N J, Louat N. The origin of fatigue fracture in copper[J]. Philosophical Magazine,1956(1):113-126.