作者：张亚涛, 刘磊, 张成银, 秦岭, 姬钰
作者单位：安徽省(水利部淮河水利委员会)水利科学研究院, 安徽 蚌埠 233000
关键词：硬化砂浆;水泥含量;粉煤灰;相对误差
摘要：
为探索处理硬化砂浆试样的方法，使水泥含量测定结果更接近真实值，首先成型不同粉煤灰掺量的砂浆试样，在砂浆试样标准养护到一定龄期后，基于硬化胶凝材料中结合水的损失过程，利用CaO测定法研究不同的试样处理方法对硬化砂浆中水泥含量测定结果的影响，得到处理硬化砂浆试样的方法：即无水乙醇终止水化后，60℃鼓风烘干，然后以10℃/min的速度由室温升到（52010）℃，保持1 h，并且通过实验证明结合水含量是影响硬化砂浆中水泥含量测定结果的关键因素之一。采用该方法处理后，不同龄期相同胶凝材料含量和同一龄期不同粉煤灰掺量硬化砂浆中水泥含量测定结果的相对误差都在5%以内。
Discussion about sample processing methods of cement content in hardened mortars
ZHANG Yatao, LIU Lei, ZHANG Chengyin, QIN Ling, JI Yu
Anhui and Huaihe River Institute of Hydraulic Research, Bengbu 233000, China
Abstract: In order to get the result that is close to the real value of cement content in hardened mortars,different samples with varied content of fly ash were prepared.After the mortar samples were cured for a certain age in a standard environment,based on the loss of bound water in hardened cementitious materials,the effect of different sample processing methods on cement content in hardened mortars was investigated via CaO measurements.The authors found an ideal processing method,that is after stopping hydration by anhydrous ethanol,sample was blast dried at 60℃,then temperature was increased from room temperature to (520±10)℃ in the rate of 10℃/min,and then maintaining for 1h.The bound water content is one of the key factors to the measurement results of cement content in hardened mortars.By using this processing method,the relative deviation of cement content of hardened mortars with different ages and fly ash content is set within±5%.
Keywords: hardened mortars;cement content;fly ash;relative deviation
2016, 42(11): 39-43 收稿日期: 2016-7-2;收到修改稿日期: 2016-7-2
基金项目: 安徽省（水利部淮河水利委员会）水利科学研究院青年科技创新基金项目（KY201404）
作者简介: 张亚涛(1983-),男,安徽亳州市人,工程师,硕士,主要从事混凝土材料研究及检测工作。
参考文献
[1] LEA F M.水泥和混凝土化学[M].3版.唐明述,胡道和,译.北京:中国建筑工业出版社.1980:732,846-849.
[2] Standard test method for Portland cement content of hardened hydraulic-cement:ASTM c1084-2002[S].2002.
[3] Methods for analysis of hardened concrete BS1881:Part 124-2013[S].2013.
[4] 李悦,童欢,杨进波.硬化混凝土原始组分测定方法综述[J].混凝土,2013(10):33-37.
[5] 徐晓云,吴双九.硬化混凝土中水泥用量的测定方法综述[J].混凝土,2009(8):103-105.
[6] LINARES L,LOPEZ-ATALAYA M,CHINCHON S.Cement content determination through selective stain in hardened concrete[J].Cement and Concrete Research,2009(39):1105-1109.
[7] SUDO E,NAKATA Y,KASAI Y,et al.Applicability of assessment method of unit cement content by sodium gluconate to hardened high-strength concrete[J].AIJ Journal of Technology and Design,2009,15(30):373-376.
[8] GOMA F,DINHERIO-ALVES M T,VICENTE M.A new procedure covering the diagnosis of hardened structural concrete in service[C]//Second International Conference on Sustainable Construction Materials and Technologies.ANCONA,2010.
[9] 李悦,童欢,杨进波,等.硬化混凝土中水泥和粗细集料用量的测定方法[J].混凝土,2015(1):147-150.
[10] LI Y,DONG W G,YANG J B,et al.Backscattered electron imaging and image analysis technology for determining the fly ash content in hardened cement mortar[J].Key Engineering Materials,2016(680):17-20.
[11] 林晖,王玲,杨柳.硬化粉煤灰水泥基材料水泥含量分析方法[J].硅酸盐通报,2014,33(4):736-740.
[12] 王智,郑洪伟,韦迎春.钙矾石形成与稳定及对材料性能影响的综述[J].混凝土,2001(6):44-56.
[13] 金祖权,孙伟,侯保荣,等.混凝土的高温变形与微结构演化[J].东南大学学报(自然科学版),2010,40(3):619-623.
[14] 韩涛,靳秀芝,王慧奇,等.高温对水泥石结构和性能的影响及机理分析[J].中北大学学报(自然科学版),2015,36(3):378-383.
[15] 马新伟,张东青,尹炜峰,等.废弃混凝土再生新技术探索[J].低温建筑技术,2009(9):4-5.
[16] 李响,阎培渝,阿茹罕.基于Ca(OH)2含量的复合胶凝材料中水泥水化程度的评价方法[J].硅酸盐学报,2009,37(10):1597-1601.
[17] 傅博,杨长辉,程臻赟.高温对碱矿渣水泥石产物及微结构的影响[J].华中科技大学学报,2013,41(5):35-38.