作者：邢琳, 曲良辉, 葛向红, 刘生满, 任海振
作者单位：中原工学院理学院, 河南 郑州 450007
关键词：镥铝石榴石;介电谱;缺陷;紫外光;偶极子
摘要：
为研究提拉法生长的镥铝石榴石单晶中的缺陷,采用波长为254 nm、功率为36 W的4根低压汞灯灯管,室温下在距离镥铝石榴石单晶样品15 cm远处对其进行紫外光辐照24 h,之后在样品上下两个7 mm7 mm表面镀上电极,置于一夹具内,夹具内部由机械泵维持真空环境,外部由液氮控制温度,利用HP4194A阻抗分析仪对紫外光辐照前后的镥铝石榴石单晶进行介电谱测试。实验结果表明:紫外光辐照后的镥铝石榴石单晶的介电损耗峰出现弛豫,由该弛豫峰对频率的依赖关系表明这种介电弛豫行为是属于偶极子取向极化的弛豫型响应,由此根据偶极子的弛豫机理推断在镥铝石榴石单晶的晶格中可能存在一定数量的缺陷。
Application of dielectric spectroscopy in lutetium aluminum garnet crystal
XING Lin, QU Lianghui, GE Xianghong, LIU Shengman, REN Haizhen
College of Science, Zhongyuan University of Technology, Zhengzhou 450007, China
Abstract: To study the defects in lutetium aluminum garnet crystal grown by Czochraski method, samples are irradiated under ultraviolet light (UV) by 4 low pressure mercury lamps (254 nm-wavelength, 36 W) placed 15 cm from the samples for 24 h at room temperature. Later, the 7 mm×7 mm surface of these samples is coated with silver films and then placed inside an evacuated cylindrical chamber, the exterior of which is submerged in liquid nitrogen during the experiment. Then, dielectric spectroscopy measurement is performed on both the irradiated and the original samples with a HP4194A impedance analyzer. The results show that the dielectric loss peaks of the irradiated samples appear relaxation effects. The dependency of these relaxation peaks on frequency indicates that the dielectric relaxation behavior is a response to the orientation polarization of a permanent dipole. It therefore can be inferred, according to the relaxation mechanism of the dipole, a certain number of defects may exist in lutetium aluminum garnet crystal.
Keywords: lutetium aluminum garnet;dielectric spectroscopy;defect;UV;dipole
2016, 42(3): 24-27 收稿日期: 2015-07-18;收到修改稿日期: 2015-09-16
基金项目: 河南省高等学校重点科研项目(15A140045);2015年中国纺织工业联合会科技指导性项目(2015020);郑州市普通科技攻关计划项目(121PPTGG363-11)
作者简介: 邢琳(1979-),女,河南南阳市人,副教授,博士,主要从事功能材料方面的研究。
参考文献
[1] PRZYBYLIИSKA H, WITTLIN A, MA C G, et al. Rare-earth antisites in lutetium aluminum garnets:Influence on lattice parameter and Ce3+ multicenter structure[J]. Optical Materials,2014,36(9):1515-1519.
[2] XING L, QU L H, HE Q, et al. Solvothermal fabrication and luminescent properties of nano LuAG:Ce phosphors[J]. Micro & Nano Letters,2014,9(1):60-63.
[3] VONDRÁŠKOVÁ A, BEITLEROVÁ A, BÁRTA J, et al. Nanocrystalline Eu-doped Lu3Al5O12 phosphor prepared by radiation method[J]. Optical Materials,2015(40):102-106.
[4] 邢琳,杨林峰. 镥铝石榴石晶体的性能及其应用[J]. 陶瓷学报,2012,32(4):621-625.
[5] XU X D, WANG X D, MENG J Q, et al. Crystal growth, spectral and laser properties of Nd:LuAG single crystal[J]. Laser Physics Letters,2009,6(9):678-681.
[6] DROZDOWSKI W, BRYLEW K, WITKOWSKI M E, et al. Effect of thermal annealing on light yield, low temperature thermoluminescence, and time profiles of LuAG:Pr scintillator crystals[J]. Radiation Measurements,2013,56(4):80-83.
[7] 殷之文. 电介质物理学[M]. 2版. 北京:科学出版社,2006: 331-332.
[8] 朱劲松,葛传珍,许自然,等. 晶体物理研究方法[M]. 南京:南京大学出版社,1990:289-302.
[9] 冯锡淇,林奇生,满振勇,等. 钨酸铅晶体的本征色心和辐照诱导色心[J]. 物理学报,2002,51(2):315-321.
[10] 冯锡淇,韩宝国,胡关钦,等. PbWO4闪烁晶体的辐照损伤机理研究[J]. 物理学报,1999,48(7):1282-1291.
[11] 沙长涛,王珂,覃承彬. 基于谐振法测试微波介质材料的介电参数[J]. 中国测试,2012,38(2):56-59.